Fire Retardant Polyurea

Fire Retardant Polyurea

Two component,100% solids,elastomeric pure polyurea membrane developed for applications requiring a fire rated coating. It is designed for situations where the coating should have excellent fire retardant and flame-resistant properties.

Product Details

Fire Retardant Polyurea

Description:

PS500B is a kind of material with high crosslinking density and certain elasticity, excellent wear resistance. This polyurea material is a high performance material with 100% solid content, double group, fast curing and field spraying molding. The product is mainly composed of isocyanate semi-prepolymer, terminal amino polyether, polyether polyol, Chain extender, pigment, with high strength, good performance, quick construction of a single molding without seams and other advantages.

Features: 

1.Fire retardant and flame resistant;

2.Without any thinner, environmental protection;

3.Elongation, high flexibility, can adapt to the basic cracks and slight deformation;

4.Good aging resistance;

5.Fast curing, can be sprayed on any surface, slope, vertical surface;

6.Convenient construction, spraying a film.

Performance:

Volume solid content

100%

Flame resistant level

BfL-s2

Hardness(shore)

90-96(A)

Density

1.02g/cm3

Elongation

330%

Tensile strength

18MPa

Impact strength

50N/mm

Water  impermeability

0.4MPa,60min

Wear resistance 750g500r

30mg

Impact  resistance

1.5kg.m

Electric strength

15kv/mm

Temperature variation

-35------+120°C

Heating  temperature

55-65°C

Water resistance30d

no rust no  bubbles no peel

Acid resistance (10%H2SO4 or 10%HCI, 30d)

no rust no  bubbles no peel

Alkali resistance  10%NaOH, 30d

no rust no bubbles  no peel

Salt resistance  60g/L, 30d

no rust no bubbles  no peel

Salt spray resistance 2000h

no rust no  bubbles no peel

Oil resistance  0# diesel crude oil 30d

no rust no  bubbles no peel

Drying time

10-20s

Touch dry time

30-50s

Flash point

200°C

Construction method:

1) Spray equipment: Spray polyurea materials must be constructed using a dedicated (1:1) two-component spray equipment. Such as Graco's H-XP3 and so on. 

2) Construction environment requirements: In order to achieve the best coating effect, the site requires ventilation, the ambient temperature should not be lower than 10 °C, the substrate temperature is higher than the dew point of 5 °C, and the air humidity is less than 80%. 

3) Surface treatment of the substrate: 

a. Leveling the cement surface: leveling the substrate with cement mortar. 

b. Grinding of the substrate: the substrate requires fine pitting (to be flat), the surface of the substrate is polished, the scar and the floating slurry are removed, and the position of the negative angle of the yin angle is treated with emphasis, and the yin angle is straight and yang. The corner suggests eight-point angle processing.

c. Cleaning: The dirt on the surface of the substrate cleaned with oil-free, water-free compressed air will clean up the debris that affects the construction of polyurea. 

4) Brush primer: brush the EP1304 or HP6303K concrete special primer, evenly brushed, no leakage coating, no defects. 

5) Scrape putty: Apply putty to seal the trachoma and micropores on the concrete surface. 

6) Spray polyurea: Spray with special polyurea spraying equipment and polyurea spray gun. Use cross method to repair leak spray and reduce stress. 

7) Spraying aliphatic polyurea topcoat: Spraying with special polyurea spraying equipment and polyurea spray gun, spraying evenly without defects and leaking spray. 

Package: Two-component, A component 220KG / 200L barrel, B component 200KG / 200L barrel. 

Color: Spray polyurea material standard color is gray, can also provide other colors according to user requirements.

Safety: Spraying polyurea materials should be equipped with basic labor protection measures during it was be used. It is recommended that operators be equipped with protective clothing, goggles, plastic gloves, masks and other protective equipment. 

Storage/Shelf Life: Ideal storage condition is 0-35 ℃ in cool and dry place, avoid direct sunlight. / One year.