Conductive Epoxy Coating

Conductive Epoxy Coating

Epoxy efficient conductive coating-Black

Product Details

Product Description:


--A two pack epoxy coating with high solid content.

--Approved by Ministry of Health of the state for use in contace with potable water.

-- Have good performance of conducuting.

--VOC less than 100g/L.

Intended Uses:

--For use in interior wall of oil tank and steel pipes antistatic anticorrosive, etc.

Product Information:

Volume   Solids:80%±2%                  Finish/Sheen  Gloss

Typical Film Thickness

125microns dry (158microns wet)

Theoretical   Coverage(m2/L)

6.4m2/L at typical   film thickness

Mix Ratio: 2.2:1volume3:1 (mass)

Method of   Application


Airless   Spray


Tip size   range:0.45-0.68mm

Output   pressure:≥17MPa

Air Spray

Tip size   range:2.0-3.0mm

Output   pressure:≥0.4MPa


For small   area only


Not   recommended. Use only in exceptional circumstances (volume 5%).



Induction   Period

Not necessary

Drying Information:  





Touch Dry




Hard Dry




Pot Life




Overcoating Data:





Overcoated by

Min Max

Min Max

Min Max


24h 10d

20h 7d

16h 5d


Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months

minimum at 25 ℃,Subject to re-inspection thereafter.

Pack Size:

Part A: 22kg/16L in 20L container

Part B: 4kg/4L in 6L container

Flash Point:

Part A: Greater than 31℃

Part B: Greater than 28℃

Mixed pant: Greater than 31℃

Systems and Compatibility:

Consult your Sunrui Representative for the systems best suited for the surfaces to be protected.

Surface Preparation:

High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.

Abrasive Blast Cleaning

Abrasive blast clean to Sa2.5(GB/T 8923.1-2011). If oxidation has occurred between blasting and application of 725-H58-01, the surface should be reblasted to the specified visual standard.

Surface defects revealed by the blast cleaning process should be ground. Filled, or treated in the appropriate manner.

Metallic Zinc Primed Surfaces

Ensure that surface of the primer is clean, dry and free from contamination and zincsalts before application of 725-H58-01. Ensure zinc primers are fully cured beforeovercoating.


The areas to be repaired should be cleaned to P St3(GB/T 8923.2-2008)by  mechanical method or higher level of surface prepared to P Sa2.5(GB/T 8923.2-2008)by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application. Overlap areas should be kept to a minimum.


1) This product will not cure adequately below 5℃. For maximum performance ambient curing temperature should be above 10℃

2) In common with all epoxy base coatings, 725-H58-01 will exhibit chalking of the firm on UV exposure.

3) Apply in good weather. Temperature of the surface to be coated must be least 3℃ above the dew point when the humidity is lower than 85%.

4) The dry time and overcoating interval may change according to the environment factors.

5)  Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.

Duty statement:

● The data in the sheet base on the information from the laboratory and practice.

● The application may exceed the control, so we only ensure our product quality.

● We own the right of the data sheet modification without informing.