Anti Static Coating For Metal

Anti Static Coating For Metal

For use in interior wall of oil tank and steel pipes antistatic anticorrosive, etc.

Product Details

725-H58-06 Epoxy Antistatic Coating-Grey

 

Product Description

-A two pack epoxy antistatic coating

-VOC less than 280g/L

Intended Uses

-For use in interior wall of oil tank and steel pipes antistatic anticorrosive, etc.

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Product Information

Volume Solids

75%±2%

Finish/Sheen

Gloss

Typical Film Thickness

125microns dry (167microns wet)

Theoretical Coverage

6m2/L at typical film thickness

Mix Ratio

4.7:1volume8:1(mass)

Method of Application

 

Airless Spray

Recommended

 

Tip size range

0.38-0.53mm

 

 

Output pressure

≥17MPa

Air Spray

Tip size range

2.0-3.0mm

 

Output pressure

≥0.3MPa

Brush/Roller

For small area only

 

Thinner

Not recommended. Use only in exceptional circumstances (volume 5%)

Cleaner

HX-501

Induction Period

Not necessary

Drying Information

 

10℃

25℃

35℃

Touch Dry

6h

2h

1h

Hard Dry

40h

24h

16h

Pot Life

8h

6h

4h

Overcoating Data           Substrate Temperature

Overcoated by

725-H58-06

10℃

25℃

35℃

Min  Max

Min  Max

Min  Max

36h   10d

24h   7d

16h   5d

Storage

Store in cool and dry conditions. Well ventilate. Keep away from hot and fire. Shelf Life: 12 months minimum at 25℃. Subject to re-inspection thereafter

Pack Size

Part A

28kg/16.5L in 20 L container

 

Part B

3.5kg/3.5L in 6L container

Flash Point

Part A

Greater than 31℃

 

Part B

Greater than 28℃

 

Mixed paint

Greater than 31℃

 

 

 

                             

 

 

 

 

 

Surface Preparation  

All surfaces to be coated should be clean, dry and free from contamination.

 

   Abrasive Blast Cleaning

 

Abrasive blast clean to Sa2½GB/T 8923.1-2011. If oxidation has occurred between blasting and application of 725-H58-06, the surface should be reblasted to the specified visual standard.

 

Surface defects revealed by the blast cleaning process should be ground. Filled, or treated in the appropriate manner.

 

   Metallic Zinc Primed Surfaces

 

Ensure that surface of the primer is clean, dry and free from contamination and zincsalts before application of 725-H58-06. Ensure zinc primers are fully cured beforeovercoating.

Repair

 

The areas to be repaired should be cleaned to St3GB/T 8923.1-2011by  mechanical method or higher level of surface prepared to Sa2.5GB/T 8923.1-2011by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application. Overlap areas should be kept to a minimum.

 

 

 

 

 

 

 

 

Limitations

 

This product will not cure adequately below 5℃. For maximum performance ambient curing temperature should be above 10℃

 

In common with all epoxy base coatings, 725-H58-06 will exhibit chalking of the firm on UV exposure.

 

Apply in good weather. Temperature of the surface to be coated must be least 3℃ above the dew point when the humidity is lower than 85%.

 

The dry time and overcoating interval may change according to the environment factors.

 

Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.

 

 

Duty statement

The data in the sheet base on the information from the laboratory and practice. The application may exceed the control, so we only ensure our product quality. We own the right of the data sheet modification without informing.