--A two pack epoxy heavy-duty anticorrosive coating and it is characterized by good adhesion and excellent resistance to chemicals, water and corrosion.
--VOC less than 180g/L
--For use in heavy-duty anticorrosive areas.
--For steel ortidal range zone of concrete stakes heavy-duty anticorrosion.
--For interior circulatory water piles of power plant special strengthening anticorrosion
--For interior wall of steel pipes and concrete of Sewage treatment works, power plants and chemical plants etc. heavy-duty anticorrosion.
--For works of tap water and water anticorrosion
Typical Film Thickness
500 microns dry（530 microns wet）
1.9m2/L at typical film thickness
Method of Application
Overcoating Data Substrate Temperature
Store in cool and dry conditions. Well ventilate. Keep away from hot and fire. Shelf Life: 12 months minimum at 25℃. Subject to re-inspection thereafter
30kg/15.5L in 20L container
4.3kg/4.5L in 6L container
Greater than 31℃
Greater than 29℃
Greater than 31℃
Consult your Sunrui Representative for the systems best suited for the surfaces to be protected.
All surfaces to be coated should be clean, dry and free from contamination.
Abrasive Blast Cleaning for steel
Abrasive blast clean to Sa2½（GB/T 8923.1-2011）. If oxidation has occurred between blasting and application of 725-H45-ZF101G, the surface should be reblasted to the specified visual standard.
Surface defects revealed by the blast cleaning process should be ground. Filled, ortreated in the appropriate manner.
Remove loose powder of the cement, attached organisms, mud, oil or grease and other foreign matter thoroughly.
The surface can be abrade by blasting or using power tool to remove loose powder, attached organisms, mud etc. and oil can be cleaned by scour.
The areas to be repaired should be cleaned to St3（GB/T 8923.1-2011）by mechanical method or higher level of surface prepared to Sa2.5（GB/T 8923.1-2011）by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application. Overlap areas should be kept to a minimum.
The areas to be repaired should be remove loose powder of the cement, attached organisms, mud, oil or grease and other foreign matter thoroughly. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application. Overlap areas should be kept to a minimum.
Apply in good weather. Temperature of the surface to be coated must be least 3℃ above the dew point when the is lower than 85%.
In common with all epoxy base coatings, 725-H45-ZF101G will exhibit chalking of the firm on UV exposure.
The dry time and overcoating interval may change according to the environment factors.
Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.
Duty statement:The data in the sheet base on the information from the laboratory and practice. The applica tion may exceed the control, so we only ensure our product quality. We own the right of the data sheet modification without informing.